  • The effects of bath composition, process conditions and other factors on the internal stress and hardness of Ni-W alloy coating were investigated, and the coating with low internal stress and high hardness was prepared for tribochemical polishing of diamond. The effects of sodium tungstate concentration, complexing agent concentration, solution PH, saccharin sodium concentration on the internal stress, tungsten content, hardness and deposition rate of the coating were investigated by single experiment, and the leveling effect of different additives on the coating roughness was explored. Finally, under the conditions of sodium tungstate 40 g/L, sodium citrate 120 g/L, saccharin sodium 1 g/L, and solution PH of 6, a Ni-W alloy disk with hardness of 713 hv and thickness of 0.7 mm was prepared by using the reverse pulse method and salicylaldehyde as the leveling agent. The polishing disc is used to conduct tribochemical polishing of diamond, and the process conditions are studied. When the speed of the polishing disc is 8000 rpm (linear speed 19.3 m/s), and the pressure is about 4.4 MPa, the polishing effect is good, and the removal rate is 5.56 μ M/min, and the grinding ratio reaches 0.394, and the surface roughness is Ra 3.693 nm. Compared with the cast iron disk, the performance of nickel tungsten alloy disk is much higher.

     

  • loading
  • 加载中

Catalog

    通讯作者: 陈斌, bchen63@163.com
    • 1. 

      沈阳化工大学材料科学与工程学院 沈阳 110142

    1. 本站搜索
    2. 百度学术搜索
    3. 万方数据库搜索
    4. CNKI搜索

    Article Metrics

    Article views (124) Cited by()
    Proportional views
    Related

    /

    DownLoad:  Full-Size Img  PowerPoint
    Return
    Return