DAI Mengjiao, CHEN Guomei, NI Zifeng, ZHANG Ping, QIAN Shanhua, BIAN Da. Preparation of homogeneous sub-micron cerium oxide polishing powder[J]. Diamond &Abrasives Engineering, 2022, 42(4): 428-432. doi: 10.13394/j.cnki.jgszz.2021.0117
Citation: DAI Mengjiao, CHEN Guomei, NI Zifeng, ZHANG Ping, QIAN Shanhua, BIAN Da. Preparation of homogeneous sub-micron cerium oxide polishing powder[J]. Diamond &Abrasives Engineering, 2022, 42(4): 428-432. doi: 10.13394/j.cnki.jgszz.2021.0117

Preparation of homogeneous sub-micron cerium oxide polishing powder

doi: 10.13394/j.cnki.jgszz.2021.0117
  • Received Date: 2021-11-25
  • Accepted Date: 2022-01-09
  • Rev Recd Date: 2021-12-30
  • To obtain homogeneous submicron cerium dioxide (CeO2) polishing powder, CeO2 was synthesized by solvothermal reaction using cerium nitrate (Ce(NO3)3·6H2O) as cerium resource and alcohol-water mixed solution as solvent. The phase composition and morphology of CeO2 were characterized by X-ray diffraction (XRD), laser particle size analyzer and scanning electron microscope (SEM). The formation process of CeO2 particles was analyzed by changing the concentration of Ce3+ and alcohol-water ratio. The synthesized CeO2 was used for chemical mechanical polishing (CMP) Si-face of 6H-SiC. The polishing characteristics were tracked by atomic force microscopy (AFM) and electronic balance. The results indicates that when the Ce3+ concentration is 0.10 mol/L and alcohol/water volume ratio is 3∶1, the as-prepared particles have regular morphology, moderate particle size and uniform particle size distribution. After polished by using the as-prepared CeO2, the Ra of wafer surface reached 0.243 nm and the dMRR 287 nm/h. The as-prepared CeO2 can be used for chemical mechanical polishing.


  • loading
  • [1]
    MIGANI A, VAYSSILOY G N, BROMLEY S T, et al. Greatly facilitated oxygen vacancy formation in ceria nanocrystallites [J]. Chemical Communications,2010,46(32):5936-5938.
    耿九光, 臧文杰, 李毅, 等. 纳米二氧化铈的制备及光催化性能 [J]. 化工进展,2014,33(3):720-723. doi: 10.3969/j.issn.1000-6613.2014.03.034

    GENG Jiuguang, ZANG Wenjie, LI Yi, et al. Preparation and photocatalytic performance of nano-ceria [J]. Chemical Industry and Engineering Progress,2014,33(3):720-723. doi: 10.3969/j.issn.1000-6613.2014.03.034
    王延泽. 晶界对二氧化铈中氧离子自扩散及导电性能的影响 [D]. 秦皇岛: 燕山大学, 2020.

    WANG Yanze. The effect of grain boundary on self-diffusion and conductivity of oxygen ions in cerium dioxide [D]. Qinhuangdao: Yanshan University, 2020.
    CHEN G, NI Z, XU L, et al. Performance of colloidal silica and ceria based slurries on CMP of Si-face 6H-SiC substrates [J]. Applied Surface Science,2015,359:664-668. doi: 10.1016/j.apsusc.2015.10.158
    李静, 常民民, 孙明艳, 等. 水热-煅烧法制备亚微米CeO2抛光粉 [J]. 中国稀土学报,2016,34(1):44-49. doi: 10.11785/S1000-4343.20160107

    LI Jing, CHANG Minmin, SUN Mingyan, et al. Preparation of submicron ceria polishing powder via hydrothermal-calcination method [J]. Journal of the Chinese Society of Rare Earths,2016,34(1):44-49. doi: 10.11785/S1000-4343.20160107
    蒋建忠, 赵永武. 一种新型的机械化学抛光模型 [J]. 江南大学学报,2007,6(5):578-582.

    JIANG Jianzhong, ZHAO Yongwu. A new model for chemical mechanical polishing [J]. Journal of Jiangnan University,2007,6(5):578-582.
    赵敏, 刘文杰. 氧化铈抛光粉粒度分级控制研究 [J]. 中国化工贸易,2013,5(8):387. doi: 10.3969/j.issn.1674-5167.2013.08.361

    ZHAO Min, LIU Wenjie. Study on particle size grading control of cerium oxide polishing powder [J]. China Chemical Trade,2013,5(8):387. doi: 10.3969/j.issn.1674-5167.2013.08.361
    TYRPEKL V, MARKOVA P, DOPITA M, et al. Cerium oxalate morphotypes: Synthesis and conversion into nanocrystalline oxide [J]. Inorganic Chemistry,2019,58(15):10111-10118. doi: 10.1021/acs.inorgchem.9b01250
    ZHOU C, ZHU D, WANG D, et al. Synthesis and characterization of cerium dioxide nanoparticles obtained by a novel soft mechanochemical method combined with sol-gel method [J]. Nano Brief Reports and Reviews,2016,12(2):1-8. doi: 10.1142/S1793292017500205
    许伟, 林泽慧, 胡鹏飞, 等. 纳米氧化铈的可控合成及其抛光性能的研究 [J]. 山东化工,2020,49(2):30-32. doi: 10.3969/j.issn.1008-021X.2020.02.011

    XU Wei, LIN Zehui, HU Pengfei, et al. Controllable synthesis and polishing properties of ceria behavior of ceria nanoparticles [J]. Shandong Chemical Industry,2020,49(2):30-32. doi: 10.3969/j.issn.1008-021X.2020.02.011
    郝顺利, 王新, 崔银芳, 等. 纳米粉体制备过程中粒子的团聚及控制方法研究 [J]. 人工晶体学报,2006,35(2):342-346. doi: 10.3969/j.issn.1000-985X.2006.02.031

    HAO Shunli, WANG Xin, CUI Yinfang, et al. Investigation on the agglomerate mechanism and controlling method in nano-particle powder preparation [J]. Journal of Synthetic Crystals,2006,35(2):342-346. doi: 10.3969/j.issn.1000-985X.2006.02.031
    CHEN H, CHANG H. Homogeneous precipitation of cerium dioxide nanoparticles in alcohol/water mixed solvents [J]. Colloids & Surfaces A Physicochemical & Engineering Aspects,2004,242(1/2/3):61-69.
    ZHOU F, ZHAO X, XU H, et al. CeO2 spherical crystallites:   Synthesis, formation mechanism, size control, and electrochemical property study [J]. The Journal of Physical Chemistry C,2007,111(4):1651-1657. doi: 10.1021/jp0660435
    田皓, 崔建国, 王荣, 等. 强化沉淀反应结晶过程制备纳米稀土氧化物的工艺开发 [J]. 中国稀土学报,2020,186(4):467-473.

    TIAN Hao, CUI Jianguo, WANG Rong, et al. Technology development of preparation of nanometer rare earth oxides by chemical enhanced process in precipitation crystallization [J]. Journal of the Chinese Society of Rare Earths,2020,186(4):467-473.
    李向果, 郭淼, 姚会敏, 等. 菱形二氧化铈的水热合成及发光机理研究 [J]. 无机盐工业,2020,52(6):30-35. doi: 10.11962/1006-4990.2019-0407

    LI Xiangguo, GUO Miao, YAO Huimin, et al. Research on hydrothermal synthesis and photoluminescence mechanism of rhombus CeO2 [J]. Inorganic Chemical Industry,2020,52(6):30-35. doi: 10.11962/1006-4990.2019-0407
  • 加载中


    通讯作者: 陈斌,
    • 1. 

      沈阳化工大学材料科学与工程学院 沈阳 110142

    1. 本站搜索
    2. 百度学术搜索
    3. 万方数据库搜索
    4. CNKI搜索

    Figures(7)  / Tables(1)

    Article Metrics

    Article views (154) PDF downloads(18) Cited by()
    Proportional views


    DownLoad:  Full-Size Img  PowerPoint